Mingtai 6082 T651 aluminum plate advantages:
Mingtai 6082 T651 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of 6000 series alloys. Alloy 6082 T651 is known as a structural alloy. In plate form, 6082 is the alloy most commonly used for machining. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy.
Properties
|
Physical Property |
Value |
|
Density |
2.70 g/cm³ |
|
Melting Point |
555°C |
|
Thermal Expansion |
24 x10^-6 /K |
|
Modulus of Elasticity |
70 GPa |
|
Thermal Conductivity |
180 W/m.K |
|
Electrical Resistivity |
0.038 x10^-6Ω.m |
|
Plate - 6.00m to 12.5mm |
Spec: BS EN 485-2:2008 |
|
Mechanical Property |
Value |
|
Proof Stress |
255 Min MPa |
|
Tensile Strength |
300 Min MPa |
|
Elongation A50 mm |
9 Min % |
|
Hardness Brinell |
91 HB |
|
Plate - 12.5mm to 100.00mm |
Spec: BS EN 485-2:2008 |
|
Mechanical Property |
Value |
|
Proof Stress |
240 Min MPa |
|
Tensile Strength |
295 Min MPa |
|
Hardness Brinell |
89 HB |
|
Plate - 100.00mm to 150.00mm |
Spec: BS EN 485-2:2008 |
|
Mechanical Property |
Value |
|
Proof Stress |
240 Min MPa |
|
Tensile Strength |
275 Min MPa |
|
Hardness Brinell |
84 HB |
|
Elongation A |
6 Min % |