6063 Aluminum Round Bar
The Introduction of 6063 aluminum round bar
6063 aluminum bars belong to low-alloy Al-Mg-Si series high plasticity alloys, known for their excellent surface finish, with excellent extrusion performance, good corrosion resistance and comprehensive mechanical properties, and are susceptible to oxidization discoloration.
The Product Features of 6063 aluminum Round Bar
● Strengthened through heat treatment with high impact toughness and insensitive to notches.
● Excellent thermoplasticity, can be extruded at high speeds into complex structural shapes, thin-walled and hollow sections, or forged into complex structural forgings.
● Excellent weldability and corrosion resistance with no tendency to stress corrosion cracking. Among heat-treatable aluminum alloys, Al-Mg-Si alloys are the only alloys where stress corrosion cracking has not been observed.
● Processed surfaces are very smooth and readily anodized and colored.
The Product Specification of 6063 aluminum round bar
| Category | Specification | Details / Typical Value |
|---|---|---|
| Standard | GB/T (China) | GB/T 3191-2019 |
| Equivalent Standards | ISO / EN / ASTM | 6063 (ISO/Aligned), EN AW-6063, AA 6063 |
| Chemical Composition | Si | 0.20 - 0.60 % |
| Fe | ≤ 0.35 % | |
| Cu | ≤ 0.10 % | |
| Mn | ≤ 0.10 % | |
| Mg | 0.45 - 0.90 % | |
| Cr | ≤ 0.10 % | |
| Zn | ≤ 0.10 % | |
| Ti | ≤ 0.10 % | |
| Al | Balance | |
| Temper | Common Tempers | T5, T6, T832, O |
| Diameter Range | Common Size | 30mm - 200 mm (varies by manufacturer) |
| Mechanical Properties (T5 Temper) | Tensile Strength | ≥ 160 MPa |
| Yield Strength (0.2% Offset) | ≥ 110 MPa | |
| Elongation (δ5) | ≥ 8 % | |
| Mechanical Properties (T6 Temper) | Tensile Strength | ≥ 205 MPa |
| Yield Strength (0.2% Offset) | ≥ 170 MPa | |
| Elongation (δ5) | ≥ 10 % | |
| Key Characteristics | Excellent Extrudability, Good Surface Finish, Good Corrosion Resistance, Moderate Strength |
Send A Message
Hot Products
6063 Aluminum Round Bar
6063 aluminum bars belong to low-alloy Al-Mg-Si series high plasticity alloys, known for their excellent surface finish, with excellent extrusion performance, good corrosion resistance and comprehensive mechanical properties, and are susceptible to oxidization discoloration.5052 Aluminum Round Bar
5052 Aluminum Bars are made with an alloy mixture of Aluminum with chromium and magnesium mixed in the ratio of 2.5% magnesium and 0.25% chromium. The Magnesium content helps the bars to have better performance at low-temperature applications and the chromium content helps the ASTM B221 Aluminum 5052 Bars to have better resistivity against corrosion in various corrosive environments.2A14 Aluminum Round Bar
2A14 aluminum round bar is a high-strength, heat-treatable aluminum alloy, belonging to the Al-Cu-Mg series, known for excellent strength, good cutting, and welding performance in its quenched and aged state.2A12 Aluminum Round Bar
2A12 aluminum bar, also known as high-strength duralumin, is a typical duralumin alloy in the AL-Cu-Mg system and can be strengthened by heat treatment. At the same time, its composition is relatively reasonable, and its overall performance is good.Henan Mingtai AL. Industrial Co.. Ltd.© All rights reserved Privacy